primary lithium battery lsh 20 3.6 v primary lithium-thionyl chloride (li-socl 2 ) high power d-size spiral cell october 2006 benefits high voltage response, stable during most of the lifetime of the application high drain/pulse capability wide operating temperature range (-60?/+85?) easy integration into compact systems low self-discharge rate (less than 3% after 1 year of storage at +20?) key features stainless steel container hermetic glass-to-metal sealing built-in safety vent finish with 5 a fuse non-flammable electrolyte underwriters laboratories (ul) component recognition (file number mh 12609) restricted for transport (class 9) main applications radiocommunication and other military applications alarms and security systems beacons and emergency location transmitters gps metering systems sonobuoys tracking systems gsm communication nato stock number 6135 14 440 1213 cell size references um1 ?r20 ?d electrical characteristics (typical values relative to cells stored for one year or less at + 30? max.) nominal capacity 13.0 ah (at 15 ma + 20? 2.0 v cut off. the capacity restored by the cell varies according to current drain, temperature and cut off) open circuit voltage (at + 20?) 3.67 v nominal voltage (at 2 ma + 20?) 3.6 v pulse capability: typically up to 4000 ma (4000 ma/0.1 second pulses, drained every 2 mn at + 20? from undischarged cells with 10 ? base current, yield voltage readings above 3.0 v. the readings may vary according to the pulse characteristics, the temperature, and the cell's previous history. fitting the cell with a capacitor may be recommended in severe conditions. consult saft) maximum recommended continuous current 1800 ma (to maintain cell heating within safe limits. battery packs may imply lower level of maximum current and may request specific thermal protection. consult saft) storage (recommended) + 30? (+ 86?) max (for more severe conditions, consult saft) operating temperature range - 60?/+ 85? (operation above ambient t may lead to reduced capacity and (- 76?/+ 185?) lower voltage readings at the beginning of pulses. operation with current continuously above 1 a may restrict upper t range. consult saft) physical characteristics diameter (max) 33.4 mm (1.32 in) height (max) 61.6 mm (2.42 in) typical weight 100 g (3.5 oz) li metal content approx. 3.8 g available termination suffix cn, cnr radial tabs cna (ax) axial leads fl flying leads ...etc.
lsh 20 saft specialty battery group 12, rue sadi carnot 93170 bagnolet - france tel +33 (0)1 49 93 19 18 fax +33 (0)1 49 93 19 69 www.saftbatteries.com storage the storage area should be clean, cool (preferably not exceeding + 30 ?), dry and ventilated. warning fire, explosion and burn hazard. do not recharge, short circuit, crush, disassemble, heat above 100? (212?), incinerate, or expose contents to water. do not solder directly to the cell (use tabbed cell versions instead). doc. n o 31015-2- 1006 information in this document is subject to change without notice and becomes contractual only after written confirmation by saft. for more details on primary lithium technologies please refer to primary lithium batteries selector guide doc n o 31048-2. published by the communications department. photo credit: saft soci?t? anonyme au capital de 31 944 000 rcs bobigny b 383 703 873 produced by arthur associates current (ma) voltage plateau versus current and temperature (at mid-discharge) time (hours) typical discharge profiles at + 20? current (ma) restored capacity versus current and temperature (2.0 v cut off) cell voltage (v) cell voltage (v) capacity (ah) dimensions in mm. 33.1 0.3 2.1 0.2 61.0 0.6 0.5 9.3 0.1 (on flat su rface) 18.0 0.2 (on flat su rface)
|
